Deformation aging is more harmful to the ductility and toughness of
low carbon steel than quenching aging, and there are obvious upper
and lower yield points on the tensile curve of low carbon steel.
From the appearance of the upper yield point to the end of yield
extension, a surface corrugation band, called Luders zone, is
formed on the surface of the sample due to uneven deformation. Many
stamping parts are often scrapped as a result. There are two ways
to prevent it. A high pre-deformation method, pre-deformation of
steel placed for a period of time after stamping will also produce
luders zone, so the pre-deformation of steel before stamping place
time should not be too long. The other is to add aluminum or
titanium to the steel to form a stable compound with nitrogen that
prevents the formation of deformation aging caused by the Collarian
gas mass.
1. Advantages:
| 1. Reasonable price with excellent quality |
| 2. Abundant stock and prompt delivery |
| 3. Rich supply and export experience, sincere service |
2. Material:
A36, A53, ASTM A106, JIS S400, Q235B, Q235C, Q235D, Q345E, Q345,
Q390B, Q390C, Q390D, Q390E, Q420, Q420B, Q420C, Q420D, Q420E, Q460,
Q460D, Q500C, Q500D, Q550C, Q550D, Q550E, Q620C, Q620D, Q620E,
Q690A, Q690B, Q690C, Q690D, Q690E, Q690D, Q690C, Q890C, Q890D,
16Mo3, 16MnL, 16MnR , 16Mng, 16MnDR
3. Chemical Composition:
| Grade | Rank | Chemical Composition( %) |
| C | Mn | Si | S | P |
| Q215 | A | 0.09~0.15 | 0.25~0.55 | ≤0.3 | ≤0.05 | ≤0.045 |
| B | ≤0.045 |
| Q235 | A | 0.14~0.22 | 0.30~0.65 | ≤0.3 | ≤0.05 | ≤0.045 |
| B | 0.12~0.20 | 0.30~0.70 | ≤0.045 |
| C | ≤0.18 | 0.35~0.80 | - | ≤0.04 | ≤0.04 |
| D | ≤0.17 | ≤0.035 | ≤0.035 |
| Q255 | A | 0.18~0.28 | 0.40~0.70 | ≤0.3 | ≤0.05 | ≤0.045 |
| B | ≤0.045 | |
| Q275 | | 0.28~0.38 | 0.50~0.80 | ≤0.35 | ≤0.05 | ≤0.045 |
4. Standard:
| Standard | Grade | General Size | Delivery Condition |
| ASTM A36 | A36/A36-B | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| ASTM A283 | A283-B/A283C | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| ASTM A572 | A572Gr50-B/A572Gr42-B | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| ASTM A515 | A515Gr70 | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| ASTM A516 | A516Gr70 | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| JIS G 3101 | SS400-B | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| JIS G3136 | SN400B | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| EN10025-2:2004 | S235JR-S355K2+N | 5-20 * 2300-2500 * C | Boron added or Black Condition |
| EN10025-5:2004 | S355J2W/S355K2W | 5-20 * 2300-2500 * C | Boron added or Black Condition |
5. Packing:
Standard stainless steel shipping packaging or as customer
required.